2010/12/14 by Edwin J. Koerperick, Edwin J Koerperick, Dennis T. Norton +7 · 1 citation
Physics and Astronomy · Engineering · #Semiconductor Quantum Structures and Devices #Advanced Semiconductor Detectors and Materials #Nanowire Synthesis and Applications
paper · doi:10.1109/jqe.2010.2072492
Superlattice InAs/GaSb light-emitting diodes with peak emission wavelength of 8.6 μm and output power approaching 190 μW at 77 K from a 120 × 120 μm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> mesa are demonstrated. Output power in excess of 600 μ.W was demonstrated from a 520 × 520 μm mesa at 1 A drive current and 50% duty cycle. Devices were grown by molecular beam epitaxy on lightly n-doped GaSb substrates and employed a 16-stage cascaded active region configuration to improve current efficiency and increase optical output. Emitting regions were coupled by semi-metallic tunnel junctions consisting of a p-GaSb layer and a thickness-graded InAs/GaSb superlattice stack.