Materials Science · Physics and Astronomy · #Advanced Condensed Matter Physics #FOS: Physical sciences #Magnetic and transport properties of perovskites and related materials #Multiferroics and related materials #Strongly Correlated Electrons (cond-mat.str-el) #Superconductivity (cond-mat.supr-con) #cond-mat.str-el #cond-mat.supr-con
paper · pdf · doi:10.48550/arxiv.cond-mat/0406586
Accepted for publication in Chem. Mater
arxiv created 2004/06/24 · openalex publication_date 2004/06/24 · arxiv updated 2009/12/01 · openalex created_date 2016/06/24 · openalex updated_date 2026/07/28
The tri-layered perovskite Sr4Rh3O10 is reported for the first time. High-pressure and high-temperature heating (6 GPa and 1500 C) brought about successful preparation of a polycrystalline sample of the expected member at n=3 of Srn+1RhnO3n+1. Neutron-diffraction studies revealed the orthorhombic crystal structure (Pbam) at room temperature and 3.4 K. Local structure distortions rotationally tilt the RhO6 octahedra ~12 degrees in the perovskite-based blocks along the c-axis, and approximately a 20 % disorder was found in sequence of the alternating rotational tilt. The sample was also investigated by measurements of specific heat, thermopower, magnetic susceptibility, and electrical resistivity. The data clearly revealed enhanced paramagnetism and electrically conducting character, which reflected nature of the correlated 4d5-electrons of Rh4+. However, no clear signs of magnetic and electrical transitions were observed above 2 K and below 70 kOe, providing a remarkable contrast to the rich electronic phenomena for the significantly relevant ruthenate, Sr4Ru3O10.