2024/05/18 by Afaak Lakouader, Lakouader, Afaak, Youness Hadouch +25
Materials Science · Physics and Astronomy · #Magnetic and transport properties of perovskites and related materials #Magnetic Properties of Alloys #Advanced Condensed Matter Physics
paper · pdf · doi:10.48550/arxiv.2405.11269
In this work, La0.8Sr0.2MnO3 (LSMO) nanopowders are synthesized using two different methods: Pechini (LSMO-PC) and auto-combustion (LSMO-AC). Nanoparticle sizes, structural, magnetic, and magnetocaloric properties were determined and compared. The X-ray diffraction confirms the coexistence of two phases; rhombohedral symmetry with space group R-3c and orthorhombic symmetry with space group Pbnm, with the rhombohedral phase dominating. The scanning electron microscope images show that LSMO-PC has larger nanoparticle sizes (~495 nm) than LSMO-AC (~195 nm). The samples exhibit ferromagnetic properties with distinct hysteresis loops and Curie temperatures 340 K and 290 K for LSMO-PC and LSMO-AC respectively. The variation of the magnetic entropy was measured indirectly using the Maxwell approach with increasing magnetic field. For LSMO-PC it reaches a maximum -dSM=1.69 J/kg.K at 340 K and dH= 5 T. The associated adiabatic temperature change dTM is 1.04 K. While LSMO-PC demonstrates superior magnetic and magnetocaloric properties, LSMO-AC displays significant magnetocaloric thermal stability. The obtained values make LSMO-PC and LSMO-AC promising candidates for eco-friendly room-temperature magnetocaloric applications.