2007/03/04 by Zhang, Y., Yang, H. X., Ma, C. +2
#FOS: Physical sciences #Materials Science (cond-mat.mtrl-sci) #Strongly Correlated Electrons (cond-mat.str-el)
paper · doi:10.48550/arxiv.cond-mat/0703102
Microstructure properties, phase transitions, and charge ordering in the LuFe2O4 materials have been extensively investigated by means of transmission electron microscopy (TEM). The (001) twins as a common defect frequently appear in the LuFe2O4 crystals along the c-axis direction, and the crystals across each boundary are rotated by 180 degree with respect to one another. The in-situ cooling TEM observations reveal remarkable temperature dependence of the superstructures in correlation with charger ordering (CO). The Fe2+, Fe3+, and Fe+2.5 ions are found to be crystallized in ordered stripes at the frustrated ground state characterized by a modulation with the wave vector of q1 =(1/3 1/3 2). In-situ heating TEM observations on LuFe2O4 clearly demonstrate that this modulation becomes evidently invisible above a critical temperature of about Tc=530K. These facts suggest that the CO should be the essential driving force for the structural transitions and ferroelectricity observed in present system.