Engineering · Physics and Astronomy · #Electrical engineering #Engineering #Engineering physics #Field-effect transistor #Force Microscopy Techniques and Applications #Materials science #Molecular Junctions and Nanostructures #Nanotechnology #Nanowire Synthesis and Applications #Optoelectronics #Physics #Silicon #Transistor #cond-mat.mes-hall
paper · pdf · doi:10.1021/acs.jpcc.6b00336
published as J. Phys. Chem. C 120, 11180-11191 (2016) · Paper and supporting information, J. Phys. Chem. C, 2016
openalex publication_date 2016/04/27 · arxiv created 2016/05/20 · arxiv updated 2016/06/16 · openalex created_date 2025/10/10 · openalex updated_date 2026/08/05
Surface characterizations of an organophosphorus (OP) gas detector based on chemically functionalized silicon nanoribbon field-effect transistor (SiNR-FET) were performed by Kelvin probe force microscopy (KPFM) and time-of-flight secondary-ion mass spectrometry (ToF-SIMS) and were correlated with changes in the current–voltage characteristics of the devices. KPFM measurements on FETs allow us (1) to investigate the contact potential difference (CPD) distribution of the polarized device as a function of the gate voltage and the exposure to OP traces and (2) to analyze the CPD hysteresis associated with the presence of mobile ions on the surface. The CPD measured by KPFM on the silicon nanoribbon was corrected because of side capacitance effects in order to determine the real quantitative surface potential. Comparison with macroscopic Kelvin probe (KP) experiments on larger surfaces was carried out. These two approaches were quantitatively consistent. An important increase of the CPD values (between +399 mV and +302 mV) was observed after the OP sensor grafting, corresponding to a decrease of the work function, and a weaker variation after exposure to OP (between −14 mV and −61 mV) was measured. Molecular imaging by ToF-SIMS revealed OP presence after SiNR-FET exposure. The OP molecules were essentially localized on the Si-NR confirming effectiveness and selectivity of the OP sensor. A prototype was exposed to Sarin vapors and succeeded in the detection of low vapor concentrations (40 ppm).