2021/03/07 by R. Teruel-Juanes, Roberto Teruel‐Juanes, Carmen del Río +6
Engineering · Energy · #Fuel Cells and Related Materials #Electrocatalysts for Energy Conversion #Advanced battery technologies research
paper · doi:10.1002/app.50671
Abstract A set of styrene‐ethylene‐butylene‐styrene triblock copolymer (SEBS) membranes with 10 or 25 wt% divinyl‐benzene (DVB) as a crosslinking agent were prepared and validated. Physicochemical characterization revealed suitable hydrolytic and thermal stability of photo‐crosslinked membranes containing 25 wt% DVB and post‐sulfonated. These compositions were evaluated in H 2 /O 2 single cells, and electrical and proton conductivities were furtherly assessed. The membranes with the milder post‐sulfonation showed greater proton conductivity than those with excessive sulfonation. In terms of electrical conductivity, a universal power law was applied, and the values obtained were low enough for being used as polyelectrolytes. At the analyzed temperatures, the charge transport process follows a long‐range pathway or vehicular model. Finally, fuel cell performance revealed the best behavior for the membrane with 25 wt% DVB, photo‐crosslinked during 30 min and mild sulfonated, with a promising power density of 526 mW·cm −2 . Overall, the results obtained highlight the promising fuel cell performance of these cost‐effective triblock copolymer‐based membranes and indicate that higher sulfonation does not necessarily imply better power density.