2008/03/04 by Monika Mudgel, V. P. S. Awanaa, V. P. S. Awana +4 · 2 citations
Materials Science · Physics and Astronomy · #Iron-based superconductors research #Physics of Superconductivity and Magnetism #Superconductivity in MgB2 and Alloys #cond-mat.str-el #cond-mat.supr-con
paper · pdf · doi:10.1016/j.ssc.2008.03.009
14 pages Text+Figs; Comments/suggestions welcome ([email protected])
arxiv created 2008/03/04 · openalex publication_date 2008/03/10 · arxiv updated 2009/12/01 · openalex created_date 2025/10/10 · openalex updated_date 2026/07/28
We report the synthesis and variation of superconductivity parameters such as transition temperature Tc, upper critical field Hc, critical current density Jc, irreversibility field Hirr and flux pinning parameter (Fp) for the MgB2-xCx system with nano-Carbon doping up to x=0.20. Carbon substitutes successfully on boron site and results in significant enhancement of Hirr and Jc(H). Resistivity measurements reveal a continuous decrease in Tc under zero applied field, while the same improves remarkably at higher fields with an increase in nano-C content for MgB2-xCx system. The irreversibility field value (Hirr) is 7.6 & 6.6 Tesla at 5 and 10K respectively for the pristine sample, which is enhanced to 13.4 and 11.0 Tesla for x = .08 sample at same temperatures. Compared to undoped sample, critical current density (Jc) for the x=0.08 nano-Carbon doped sample is increased by a factor of 24 at 10K at 6 Tesla field.