2025/05/14 by Muzi Chen, Hanna L. B. Boström, Dominik Daisenberger +5 · 1 voice
Engineering · Materials Science · #Elasticity and Material Modeling #Fatigue and fracture mechanics #Thermal Expansion and Ionic Conductivity
paper · pdf · doi:10.1021/jacs.5c02999
openalex publication_date 2025/05/14 · openalex created_date 2025/10/10 · openalex updated_date 2026/08/01
High Resolution Image Download MS PowerPoint Slide Copper(I) tricyanomethanide, Cu(tcm), is a flexible framework material that exhibits the strongest negative area compressibility (NAC) effect ever observed─a remarkable property with potential applications in pressure sensors, artificial muscles, and shock-absorbing devices. Under increasing pressure, Cu(tcm) undergoes two sequential phase transitions (tetragonal → orthorhombic → monoclinic): It has an initial tetragonal structure ( I 4 1 md ) at ambient conditions, but this structure only persists within a narrow pressure range; at 0.12(3) GPa, a pressure-induced ferroelastic phase transition occurs, transforming Cu(tcm) into a low-symmetry orthorhombic structure ( Fdd 2). The orthorhombic phase has a NAC of −108(14) TPa –1 in the b–c plane between 0.12(3) and 0.93(8) GPa. The NAC behavior is associated with framework hinge motion in a flexible framework with “wine-rack” topology. At 0.93(8) GPa, Cu(tcm) undergoes a second phase transition and transforms into a layered monoclinic structure ( Cc ) with topologically interpenetrating honeycomb networks. The monoclinic phase of Cu(tcm) exhibits a slight negative linear compressibility (NLC) of −1.1(1) TPa –1 along the a axis and a zero area compressibility of K ac = K a + K c = 0.0(4) TPa –1 in the a – c plane over the pressure range of 0.93–2.63 GPa. In contrast to the orthorhombic phase, its mechanism is understood as the pressure-driven dampening of layer “rippling,” which acts to increase the cross-sectional area of the layer at higher hydrostatic pressures. These findings have implications for understanding the underlying mechanism of NAC phenomenon in framework materials.