Quantitative study of the corrosion evolution and stress corrosion cracking of high strength aluminum alloys in solution and thin electrolyte layer containing Cl-

2020/10/21 by Liwei Wang, Jianming Liang, Han Li +2 · 7 citations
Materials Science · Engineering · #Corrosion Behavior and Inhibition #Hydrogen embrittlement and corrosion behaviors in metals #Aluminum Alloy Microstructure Properties

paper · doi:10.1016/j.corsci.2020.109076

Cited by

• The Effect of the Modification of Mica by High-Temperature Mechanochemistry on the Anticorrosion Performance of Epoxy Coatings. [europepmc]
• Correlation between Microstructure and Hydrogen Degradation of 690 MPa Grade Marine Engineering Steel. [europepmc]
• Impact of Marine Atmospheric Corrosion on the Microstructure and Tensile Properties of 7075 High-Strength Aluminum Alloy. [europepmc]
• In Situ Electrochemical Monitoring of the Crevice Corrosion Process of the 7075-T651 Aluminium Alloy in Acidic NaCl and NaNO 3 Solution. [europepmc]
• Investigation of the Combined Influence of Temperature and Humidity on Fatigue Crack Growth Rate in Al6082 Alloy in a Coastal Environment. [europepmc]
• Deciphering and Mitigating Failure Mechanisms in Poly(ether Imide) Corrosion Protection Coatings for Automotive Light-Weighting. [europepmc]
• Study on the Mechanical Property Degradation Laws of 6061-T6 Aluminum Alloy Under the Synergistic Effect of Corrosion and Cyclic Loading. [europepmc]