2006/03/29 by B. J. Senkowicz, A. A. Polyanskii, Senkowicz, B. J. +7
Materials Science · Physics and Astronomy · #FOS: Physical sciences #Iron-based superconductors research #Physics of Superconductivity and Magnetism #Superconductivity (cond-mat.supr-con) #Superconductivity in MgB2 and Alloys
paper · pdf · doi:10.48550/arxiv.cond-mat/0603800
openalex publication_date 2006/03/29 · openalex created_date 2016/06/24 · openalex updated_date 2026/07/28
Carbon-doped magnesium diboride was fabricated from pre-reacted pure MgB2 by mechanical alloying. The sample set had excellent critical current densities Jc(8T,4.2K) ranging from 15-60 kA/cm2, depending on composition. Magneto-optical imaging detected regions up to 0.5 mm in size which were nearly 100% dense with Jc 2-6 times that of the matrix. Evaluation of resistivity curves using the Rowell method predicts that only 10-50% of the cross sectional area carries the normal state measurement current, suggesting that considerable increases in Jc in these ~80% dense MgB2 samples would be possible with complete grain and particle connectivity.