2018/05/10 by Medasani, Bharat, Sushko, Maria L., Rosso, Kevin M. +2
#FOS: Physical sciences #Materials Science (cond-mat.mtrl-sci)
paper · doi:10.48550/arxiv.1805.03775
First principles density functional theory (DFT) investigation of native interstitials and the associated self-diffusion mechanisms in α-Cr2O3 reveals that interstitials are more mobile than vacancies of corresponding species. Cr interstitials occupy the unoccupied Cr sublattice sites that are octahedrally coordinated by 6 O atoms, and O interstitials form a dumbbell configuration orientated along the [221] direction (diagonal) of the corundum lattice. Calculations predict that neutral O interstitials are predominant in O-rich conditions and Cr interstitials in +2 and +1 charge states are the dominant interstitial defects in Cr-rich conditions. Similar to that of the vacancies, the charge transition levels of both O and Cr interstitials are located deep within the bandgap. Transport calculations reveal a rich variety of interstitial diffusion mechanisms that are species, charge, and orientation dependent. Cr interstitials diffuse preferably along the diagonal of corundum lattice in a two step process via an intermediate defect complex comprising a Cr interstitial and an adjacent Cr Frenkel defect in the neighboring Cr bilayer. This mechanism is similar to that of the vacancy mediated Cr diffusion along the c-axis with intermediate Cr vacancy and Cr Frenkel defect combination. In contrast, O interstitials diffuse via bond switching mechanism. O interstitials in -1 and -2 charge states have very high mobility compared to neutral O interstitials.