Enhancement of corrosion protection efficiency of mild steel by 3,5-di(4-tolyl)-4-amino-1,2,4-triazole in hydrochloric acid medium

2020/09/11 by Tourabi, K, Nohair, K, Nyassi, N +3
#4-aminotriazole #Adsorption #Corrosion inhibition #Hydrochloric acid #Mild steel

paper · doi:10.48317/imist.prsm/morjchem-v1i2.1903

Abstract

New 3,5-disubstituted-4-amino-1,2,4-triazole derivative, namely 3,5-di(4-tolyl)-4-amino-1,2,4-triazole (4-DTAT) was synthesised and its inhibitive action against the corrosion of mild steel in 1 M HCl solution was investigated at 308 K. The detailed study of 4-DTAT was been performed using gravimetric measurements and polarisation curves method. Results show that 4-DTAT is a good inhibitor and its inhibition efficiency reaches 95 % at·10−4 M. Tafel polarisation study revealed that 4-DTAT acts as a mixed type inhibitor. The adsorption of 4-DTAT on steel surface obeyed Langmuir’s adsorption isotherm. The inhibitor adsorption process in mild steel/4-DTAT/hydrochloric acid system was studied at different temperatures (308-323 K) by means of weight loss measurements.

Related

• Aromatic Triazoles as Corrosion Inhibitors for Mild Steel in Acidic Environments
• Electrochemical and Quantum Chemical Studies of 3,5-Di(n-Tolyl)-4-Amino-1,2,4-Triazole Adsorption on Mild Steel in Acidic Media
• Triazole derivative as new and effective corrosion inhibitor for carbon steel in hydrochloric acid: Electrochemical and quantum chemical studies
• Effect of chlorine group position on adsorption behavior and corrosion inhibition of Chlorobenzylideneamino-5-methyl-2, 4-dihydro-1, 2, 4-triazole-3-thione Schiff bases: Experimental study
• Theoretical and experimental evaluation of the inhibiting power of 4-amino,5-phenyl-1,2,4-triazole,3-thione against corrosion copper in a neutral chloride environment